Abstract
A simple method for fabrication of highly ordered gold nanorod film is introduced in this article. The procedure is based on thermal evaporation of gold into a porous anodic alumina film (PAA). The PPA film was fabricated by combining the hard and mild anodization. This combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with controlled pore diameter and length. It was found that gold nanorods configuration affected by the porous anodic alumina film structure such as pore diameter and length. Furthermore the evaporation process change the rods diameter along the nanopores via the decreasing the pore mouth during the gold deposition.
Soltani, Z., Moradi, M., Noormohammadi, M., & Behzadi, F. (2012). Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores. Journal of Nanostructures, 2(2), 235-240. doi: 10.7508/jns.2012.02.012
MLA
Z. Soltani; M. Moradi; M. Noormohammadi; F. Behzadi. "Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores", Journal of Nanostructures, 2, 2, 2012, 235-240. doi: 10.7508/jns.2012.02.012
HARVARD
Soltani, Z., Moradi, M., Noormohammadi, M., Behzadi, F. (2012). 'Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores', Journal of Nanostructures, 2(2), pp. 235-240. doi: 10.7508/jns.2012.02.012
VANCOUVER
Soltani, Z., Moradi, M., Noormohammadi, M., Behzadi, F. Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores. Journal of Nanostructures, 2012; 2(2): 235-240. doi: 10.7508/jns.2012.02.012