Hydrophobic Treatment of Cotton Fabrics Using Recycled Silica Nanoparticles from Rice Bran Ash

Document Type : Research Paper

Authors

1 Physics and Chemistry Group, Faculty of Basic Sciences, Imam Ali University, Iran

2 Department of Chemical Engineering, Faculty of Engineering, Tarbiat Modares University, Tehran, Iran

3 Toxicology Research Center, Aja University of Medical Sciences, Tehran, Iran

4 Department of Chemical Engineering, University of Tehran, Tehran, Iran

5 Department of Textile Engineering, Yazd University, Yazd, Iran

Abstract

Rice bran, abundant in rice-producing countries, contains lots of silica. In this study, we recycled silica nanoparticles from rice bran ash. Then we used them to enhance the hydrophobicity of cotton fabrics. According to X-ray fluorescence (XRF) results, the recycled nanosilica had high purity (95%). The obtained results from Field Emission Scanning Electron Microscopy (FESEM) showed the structure and morphology of the powder. The particle size of the extracted nanoparticles was around 48 nm. X-Ray Diffraction (XRD) pattern showed that the extracted nanosilica has an amorphous structure. Images of Thermal Emission Microscopy (TEM) also indicated that the nanosilica has an amorphous structure. Then, the cotton fabric hydrophobicity was enhanced using siloxane compounds and recycled nanosilica. The emersion method was employed to apply the nanosilica and siloxane compounds on the fabric’s surface. (Energy Dispersive Spectroscopy) EDS examinations showed that the silica nanoparticles were evenly distributed on the surface of the cotton fabric. The water contact angle was 141, meaning that the extracted nanosilica has enhanced the hydrophobicity of cotton fabric. 

Keywords


INTRODUCTION
Nowadays, nanostructures have wide applications [1-3] and nano-synthesis has become a significant challenge. It is being performed in various branches of chemistry such as hydrophobic treatment of textiles [4-6], creating antibacterial properties on the surface of textile [7], nano-catalyst modification [8, 9], etc. 
Researchers have employed different methods to synthesize nanostructures. In some of the previous works, researchers have investigated the effects of a specific synthesis method on the morphology of the nanostructure [10, 11].For example, Masjedi-Arani et al. [11] prepared spherical silica nanostructures through the sonochemical method and investigated different parameters such as concentration, ultrasonic eave powder and reaction time on the morphology and size of the products.
Silicon dioxide (SiO2) is the most abundant compound in the earth’s crust. Silica is present in nature in free form or combination with other oxides. Silica used in industry is obtained in two ways: mineral and synthetic. In the synthetic method, materials including sedimentary silica, silica fume, nano-silica, etc., are obtained. Silica nano-particles include a set of small silicon dioxide particles that connect through covalent and hydrogen bonds and form larger particles. According to the size of the initial particles and final size of agglomerates, this compound can have different applications as nano silica or micro silica. The most crucial advantage of nanosilica is covering a large area. Its applications include rubber, paint, coating industries, adhesives, concrete and cement, plastics, paper industry, etc.
 On the other hand, rice bran considered an agricultural waste, [12] is found in abundance in rice producing countries and its ash is rich in silica [13-15]. It’s been reported that rice bran is being produced 80 million tons yearly [14, 15]. According to reports, in1997 and 1998, about 26 million tons of rice was produced in India [13, 16] and 400 thousand tons of rice bran are being produced yearly in Malaysia [17]. Also, in Egypt, 3 million tons of rice bran is being produced annually [12]. The annual increase of this product is a significant problem [18] because most farmers burn the rice bran to release its nutrients for the next planting season and get rid of its large amount. Burning rice bran leads to suffocating smoke and increased air pollution [12]. Rice bran has different applications, and it is important to recycle it. 
Researchers have tried to extract nanosilica from rice husk in some previous studies. Carmona et al.[19] burned rice husk in high temperature and pressure and extracted nanosilica through its high solubility. They used sulfuric acid, phosphoric acid, etc., as solvents. Liou et al. [20, 21], in two different studies in 2004 and 2011, also extracted nanosilica from two different types of rice with specific surface areas of 235 m2/g and 634 m2/g. In another study, Yuvakkumar et al.[22], used different concentrations of sodium hydroxide to purify nanosilica. They could extract nanosilica with a purity of 99.9% and a diameter of 25 nm using 2.5 N sodium hydroxide. The specific surface area was measured equal to 274 m2/g. These results were obtained using FTIR, TEM, BET, X-ray and particle size analyzer instrument. 
One of the most important applications of silica-based compounds is their use in the formulating water-repellent compounds and hydrophobic coatings. Hydrophobic coatings are completely transparent nonmetric coatings that can be used on different surfaces, such as glass, wood, stone, etc., and are coated on these surfaces in different ways. Hydrophobic surfaces are also observable in other creatures and parts of nature, such as Lotus leaves [23, 24], wings of some insects such as large yellow mosquitos[25], legs of water striders[26], etc. 
An applicable hydrophobic property can be created by placing silica nanoparticles in a suitable polymer substrate and functionalizing the surface of these particles. Understanding and controlling wettability are essential in both basic research and industrial applications. Modification of surface chemistry is also one of the most effective ways to control the behavior of surfaces. However, this surface chemistry modification can have limitations, such as the choice of chemical species and their biochemical compatibility [27-29]. The smoothness and comfortness of the textiles is an important issue, so when any coatings are being applied on their surface should not have any adverse effect on it. As it has been reported before, using nanoparticles affects none of the mentioned properties [30]. 
Researchers have used SiO2 many times to improve surface properties. As an example, Xue et al. [5], found out that cotton textiles are highly hydrophilic and can be completely soaked in water. When cotton textile is coated with silica hydrocele, the cotton fibers are completely coated with SiO2 nanostructure. As abundant hydroxyl groups are present on the structure of SiO2, a drop of water spreads rapidly on the surface of the coated cotton cloth. As a result, the water contact angle of the cotton cloth covered with only silica hydrocele was assumed to be zero. Hao et al.[31] after investigating the results of studies on different surfaces found out that properties of the surface change after applying PSAMS and PSAMS-SiO2. Results show that cotton fabric has a surface roughness of micrometers, and the structural changes of the surface are enhanced by coating with PSAMS and PSAMS-SiO2. The contact angle of the drop and the coated surfaces with PSAMS and PSMAS-SiO2 was reported to be 141.5 and 157, respectively. In another study, Xue et al. [6]  applied PDMS and SiO2 compounds several times on the polyester fabric to check the contact angle. They found that as the number of coatings increased, the contact angle between the droplet and the water decreased (144 to 123 degrees). With increasing the number of layers, the roughness will be greater than nanometers and micrometers, and the contact angle will be lower. The surface will not be superhydrophobic through this coating, and with increasing the number of layers the hydrostatic strength of the textile will be enhanced. In this study, nanosilica was obtained from rice bran ash (obtained from farms in Hashtpar city of Guilan province). Then it was used along with other silicon-based compounds such as Polydimethylsiloxane in preparing a suitable formulation for hydrophobization of cotton textiles. 
In most of the previous works, researchers have synthesized nanosilica. However, we have extracted nanosilica from rice bran husk in this work and used to enhance the hydrophobicity of cotton fabric’s surface. Only a few researchers have obtained nanosilica through this method, but none of them have utilized recycled nanosilica to improve the hydrophobicity of fabrics.
Mostly, chemical methods such as vapor-phase reaction, sol-gel or thermal decomposition are employed to synthesize nanosilica powder. It is easy to synthesize nanosilica with controlled shape and high purity in chemical methods, but reagents are costly [22]. It is also essential to control these specifications in large-scale industrial applications with low cost. As discussed before, rice husk, which contains more than 95% silica, is one of the most abundant by-products in the agriculture industry. So, rice husk can be a valuable source to produce nanosilica in large-scale industrial applications. 

MATERIALS AND METHODS
Materials 
Hydrochloridic acid (HCl), Sodium Hydroxide (NaOH), Sulfuric acid (H2SO4), Tetrahydrofuran (THF), Cetyltrimethylsiloxane (CTMS), Tetraetoxysiloxane (TEOS) were purchased from Merck. Polydimethylsiloxane (PDMS) was purchased from Sigma-Aldrich, and ethanol was purchased industrially. Then we washed the cotton fabrics to remove any contamination from the surface. Deionized water was employed to measure the contact angle.

Nanosilica Extraction
First, the rice bran was placed in the furnace at 700 ° C for 6 hours. Then the rice bran ash was refluxed with HCl 6 normal solution for 6 hours to remove excess metals and so on. The obtained mixture was filtered after 6 hours, and the powder was stirred with 2.5 normal NaOH. Then it was placed in an ultrasonic bath and was filtered at the end. The obtained powder was placed in boiling water, then. The pH of the mixture was adjusted using sulfuric acid (pH=2). After filtering the solution, nanosilica powder was obtained through reactions 1 and 2. Fig. 1 shows the photos of the obtained samples in each step. 
SiO2 + NaOH → Na2SiO3 + H2O                                (1)

Na2SiO3 + H2SO4 → SiO2 + Na2SO4 + H2O                (2)

Hydrophobic treatment of the fabrics
We prepared 1 gram of recycled silica. 50 ml of THF, 2.75 grams of PDMS were mixed for half an hour. The cotton fabric was cut in dimensions of 10 cm x 10 cm, washed and, dehydrated completely. The cotton textile was immersed in the solution for half of an hour. Then it was cured in the oven for 8 hours at a temperature of 135℃. We prepared a solution of 6 ml TEOS, 2 ml MTMS and 100 ml alcohol, and the fabric was immersed in this solution for 30 minutes at a temperature of 80 ℃ and dehydrated (Fig. 2). 

RESULTS AND DISCUSSION
Morphology observation of the extracted nanosilica 
To investigate the purity of the recycled nanosilica, Philips PW1410 was utilized to obtain XRF results. As it is observable in table (3.1), the recycled nanosilica has a high purity of 95%.
A Field emission scanning electron microscopy (FESEM) model FEI NOVA SEM 450 was employed to investigate the distribution and morphology of the nanosilica particles (Fig. 3). It is observable that the particle size of the obtained nanosilica is around 45 nm. It also indicates the amorphous and spherical structure and uniform morphology of nanosilica. However, a few larger particles with a 90–110 nm diameter are also observable in the image.  The formation of these large particles is because of aggregation between adjacent SiO2 nanoparticles due to their inherent high specific surface area and high surface energy[4].
XRD method was utilized for determining the phase type and amorphous structure of the recycled nanosilica. In Fig. 4, a great peak is observed in 2 θ=22, which is related to the amorphous silica. The absence of sharp peaks at this temperature is due to the absence of crystallinity. The average size of the particles was obtained 48 nanometers through Scherrer formula. The obtained XRD pattern is very similar to the XRD pattern of nanosilica in previous works (Fig. 5) [22].
A TEM image of the extracted nanosilica was also taken utilizing TEM Philips EM 208S (Fig 6.). The amorphous structure of the nanosilica is also observable in the TEM image. 
Bruker FTIR model Tensor 27 was utilized to investigate the presence of chemical groups. According to FTIR results, the main chemical groups present in extracted silica powder are shown in Fig. 7. The peak of broadband absorption in the range of 400 to 4000 cm-1 was observed in the FTIR spectrum. The absorption peak around 3427 cm-1 and 1633 cm-1 are related to O-H and H-O-H groups, respectively, and it is clear that these peaks are present due to water absorption. O-H groups and H-O-H groups indicate tensile and bending vibrations of water molecules, respectively.
The absorption peak observed in the 480 cm-1 is related to the rocking vibrations of the siloxane group (Si-O-Si), and 790 cm-1 and 1100 cm-1 regions are related to the stretching vibration of the siloxane group (Si-O-Si) [32]. 
The region with a wavenumber around 2926 cm-1 indicates C-H groups. The meager presence of this group can be because of the incomplete transformation of the rice bran, which consists of Hydrocarbon groups.
BET technique was also employed to measure the surface area of the recycled nanosilica. According to BET results specific surface area was 140.34 m2g-1, the total pure volume was 0.3786 cm3g-1, and the mean pore volume was 0.3786 cm3g-1. BET curve is presented in Fig. 8.

Treated fabrics surface observation
According to Fig. 9, FESEM photos of the fabrics coated with recycled silica, nanoparticles are distributed monotonous on the fabric surface. Most parts of the surface are covered with nanoparticles, so water drops do not have direct contact with the cotton fabrics. The air also gets trapped between the layers and avoids water drops penetrating the fabric cotton. As it is observable in Fig. 9 roughness of the fabrics has increased compared to pure cotton fabrics [30]. 
EDS analysis was also performed to investigate the distribution of elements on the fabric surface (Fig. 10). Map data of the coated compounds is also available (Fig. 11). 
The results show that silica nanoparticles have covered the surface, which leads to the high hydrophobicity of the cotton fabric surface.
 EDS results in this study were compared to those of previous works. The results had acceptable compliance with the reference sample [33]. 
Contact angle measurement was also performed using a CCD camera and Digimizer analytical software, which is mostly used to characterize surface wettability. Hydroxyl groups in the structure of untreated cotton fabrics have led to a contact angle of 0 which means they are highly water absorbent [4].  To measure the contact angle on the surface of the treated fabrics a 5 μL droplet of water was placed on its surface (Fig. 12). The contact angle was 140 degrees. The silica particles provide enough roughness to make the textile hydrophobic.

CONCLUSION 
This study aimed to investigate the possibility of hydrophobic treatment of textile using rice bran ash and silicone-based compounds such as Polydimethylsiloxane. The obtained results showed that nanosilica was extracted with high purity and coated in the cotton fabric completely. The recycled nanosilica was used for preparing hydrophobic coatings, and the results were satisfying. The hydrophobic chain of PDMS helps PDMS and SiO2 crosslink with each other. This leads to the increase of clusters with different sizes and micro-nano structure formation. Then the surface becomes more hydrophobic with the increase of roughness. According to the results, nanosilica particles had covered the fabric’s surface and were avoiding direct contact of water drops and the fabric surface. The contact angle was 140, which means the surface is entirely hydrophobic. Hydrophobicity price and time can be decreased due to using rice bran, and recycled silica from the rice bran ash can be used with siloxane compounds to increase the hydrophobicity of the cotton fabrics. 

ACKNOWLEDGMENT
We would like to thank physics and chemistry group of Imam Ali University for their support.

CONFLICT OF INTEREST
The authors declare that there is no conflict of interests regarding the publication of this manuscript.

 

 

1.    Ahmadian-Fard-Fini S, Ghanbari D, Salavati-Niasari M. Photoluminescence carbon dot as a sensor for detecting of Pseudomonas aeruginosa bacteria: Hydrothermal synthesis of magnetic hollow NiFe2O4-carbon dots nanocomposite material. Composites Part B: Engineering. 2019;161:564-577.
2.    Esmaeili-Bafghi-Karimabad A, Ghanbari D, Salavati-Niasari M, Nejati-Moghadam L, Gholamrezaei S. Photo-catalyst tin dioxide: synthesis and characterization different morphologies of SnO2 nanostructures and nanocomposites. Journal of Materials Science: Materials in Electronics. 2015;26(9):6970-6978.
3.    Gholamian F, Salavati-Niasari M, Ghanbari D, Sabet M. The Effect of Flower-Like Magnesium Hydroxide Nanostructure on the Thermal Stability of Cellulose Acetate and Acrylonitrile–Butadiene–Styrene. J Cluster Sci. 2012;24(1):73-84.
4.    Xu B, Cai Z, Wang W, Ge F. Preparation of superhydrophobic cotton fabrics based on SiO2 nanoparticles and ZnO nanorod arrays with subsequent hydrophobic modification. Surf Coat Technol. 2010;204(9-10):1556-1561.
5.    Xu L, Zhuang W, Xu B, Cai Z. Fabrication of superhydrophobic cotton fabrics by silica hydrosol and hydrophobization. Appl Surf Sci. 2011;257(13):5491-5498.
6.    Xue C-H, Li M, Guo X-J, Li X, An Q-F, Jia S-T. Fabrication of superhydrophobic textiles with high water pressure resistance. Surf Coat Technol. 2017;310:134-142.
7.    Taheri P, Khajeh-Amiri A. Antibacterial cotton fabrics via immobilizing silver phosphate nanoparticles onto the chitosan nanofiber coating. Int J Biol Macromol. 2020;158:282-289.
8.    Dehbalaei MG, Foroughifar N, Khajeh-Amiri A, Pasdar H. Ni (II) Immobilized on Fe3O4@SiO2@L-Methionine: A Reusable Nanocatalyst and its Application in the Synthesis of New Tetracyclic Tacrine Derivatives. Org Prep Proced Int. 2020;52(3):171-180.
9.    Norouzi FH, Foroughifar N, Khajeh-Amiri A, Pasdar H. A novel superparamagnetic powerful guanidine-functionalized γ-Fe2O3 based sulfonic acid recyclable and efficient heterogeneous catalyst for microwave-assisted rapid synthesis of quinazolin-4(3H)-one derivatives in Green media. RSC Advances. 2021;11(48):29948-29959.
10.    Ghanbari D, Sharifi S, Naraghi A, Nabiyouni G. Photo-degradation of azo-dyes by applicable magnetic zeolite Y–Silver–CoFe2O4 nanocomposites. Journal of Materials Science: Materials in Electronics. 2016;27(5):5315-5323.
11.    Masjedi-Arani M, Salavati-Niasari M, Ghanbari D, Nabiyouni G. A sonochemical-assisted synthesis of spherical silica nanostructures by using a new capping agent. Ceram Int. 2014;40(1):495-499.
12.    Hessien MM, Rashad MM, Zaky RR, Abdel-Aal EA, El-Barawy KA. Controlling the synthesis conditions for silica nanosphere from semi-burned rice straw. Materials Science and Engineering: B. 2009;162(1):14-21.
13.    Chandrasekhar S, Satyanarayana KG, Pramada PN, Raghavan P, Gupta TN. Review. Processing, Properties and Applications of Reactive Silica from Rice Husk — An Overview. ChemInform. 2004;35(6).
14.    Siqueira EJ, Yoshida IVP, Pardini LC, Schiavon MA. Preparation and characterization of ceramic composites derived from rice husk ash and polysiloxane. Ceram Int. 2009;35(1):213-220.
15.    Umeda J, Kondoh K. High-purity amorphous silica originated in rice husks via carboxylic acid leaching process. Journal of Materials Science. 2008;43(22):7084-7090.
16.    Chandrasekhar S, Pramada PN, Majeed J. Effect of calcination temperature and heating rate on the optical properties and reactivity of rice husk ash. Journal of Materials Science. 2006;41(23):7926-7933.
17.    Yusof AM, Nizam NA, Rashid NAA. Hydrothermal conversion of rice husk ash to faujasite-types and NaA-type of zeolites. J Porous Mater. 2009;17(1):39-47.
18.    Liou T-H, Wu S-J. Characteristics of microporous/mesoporous carbons prepared from rice husk under base- and acid-treated conditions. J Hazard Mater. 2009;171(1-3):693-703.
19.    Carmona VB, Oliveira RM, Silva WTL, Mattoso LHC, Marconcini JM. Nanosilica from rice husk: Extraction and characterization. Industrial Crops and Products. 2013;43:291-296.
20.    Liou T-H. Preparation and characterization of nano-structured silica from rice husk. Materials Science and Engineering: A. 2004;364(1-2):313-323.
21.    Liou T-H, Yang C-C. Synthesis and surface characteristics of nanosilica produced from alkali-extracted rice husk ash. Materials Science and Engineering: B. 2011;176(7):521-529.
22.    Yuvakkumar R, Elango V, Rajendran V, Kannan N. High-purity nano silica powder from rice husk using a simple chemical method. J Exp Nanosci. 2012;9(3):272-281.
23.    Barthlott W, Neinhuis C. Purity of the sacred lotus, or escape from contamination in biological surfaces. Planta. 1997;202(1):1-8.
24.    Feng L, Li S, Li Y, Li H, Zhang L, Zhai J, et al. Super-Hydrophobic Surfaces: From Natural to Artificial. Adv Mater. 2002;14(24):1857-1860.
25.    Yang W, Shi Y, Wu D, Wang Y, Feng X. Large yellow spot mosquitos favor humid conditions and display superhydrophobic properties on their wings and legs. Chin Sci Bull. 2011;56(16):1241-1245.
26.    Gao X, Jiang L. Water-repellent legs of water striders. Nature. 2004;432(7013):36-36.
27.    Juodsnukytė D, Daukantienė V, Gutauskas M. Investigating the implications of static and dynamic loading in high‐performance fabrics for outdoor clothing. International Journal of Clothing Science and Technology. 2008;20(1):7-14.
28.    Pfanner T. Military uniforms and the law of war. Revue Internationale de la Croix-Rouge/International Review of the Red Cross. 2004;86(853):93.
29.    Military Textiles. CRC Press; 2008.
30.    Jeyasubramanian K, Hikku GS, Preethi AVM, Benitha VS, Selvakumar N. Fabrication of water repellent cotton fabric by coating nano particle impregnated hydrophobic additives and its characterization. Journal of Industrial and Engineering Chemistry. 2016;37:180-189.
31.    Hao L, An Q, Xu W. Facile fabrication of superhydrophobic cotton fabric from stearyl methacrylate modified polysiloxane/silica nanocomposite. Fibers and Polymers. 2012;13(9):1145-1153.
32.    Thuadaij P, Nuntiya A. Preparation and Characterization of Faujasite using Fly Ash and Amorphous Silica from Rice Husk Ash. Procedia Engineering. 2012;32:1026-1032.
33.    Bae GY, Min BG, Jeong YG, Lee SC, Jang JH, Koo GH. Superhydrophobicity of cotton fabrics treated with silica nanoparticles and water-repellent agent. Journal of Colloid and Interface Science. 2009;337(1):170-175.