Document Type : Research Paper
Authors
1 D. Serikbayev East Kazakhstan Technical University The Republic of Kazakhstan, Ust-Kamenogorsk
2 Department of Medical Instrumentation Engineering Techniques, Imam Ja’afar Al-Sadiq University, Iraq
3 Department of anesthesia , Al-Nisour University College, Baghdad, Iraq
4 Department of Pharmacology, College of Pharmacy, University of Al-Ameed, Karbala, Iraq
5 Department of Optical Techniques, AlNoor University College, Iraq
6 Department of Optical Techniques, Al-Hadi University College, Baghdad, 10011, Iraq
7 Department of Pharmacy, Al-Manara College For Medical Sciences/ (Maysan), Iraq
8 College of Medical Technology, Medical Lab techniques, National University of Science and Technology, Dhi Qar, Iraq
9 Bukhara State Medical Institute, Uzbekistan
10 Termiz State University, Uzbekistan
11 Abai Kazakh National Pedagogical University, Dostyk 13. Almaty, Kazakhstan
Abstract
Keywords
INTRODUCTION
Metal oxide nanoparticles are a significant type of nanomaterials widely utilized in various industries [1-3]. Among these, zinc oxide nanoparticles (ZnO NPs) hold great importance in medicine, pharmacy, and other sectors [4]. ZnO NPs are extensively utilized in the manufacturing of nanoscale materials, following silver oxide, titanium dioxide, and silicon dioxide nanoparticles [5]. The collective production of 41 different nano-products using ZnO NPs is estimated to exceed 600 tons annually [6,7]. These nanoparticles are typically synthesized through chemical methods. However, their excessive application has resulted in the generation of nano-sewage, with a substantial portion entering aquatic environments, estimated to be over 410,000 tons per year [8].
The presence of nanoparticles in water has led to genetic alterations and elevated mortality rates among aquatic organisms, including fish [9]. Additionally, the chemical processes involved in nanoparticle production have proven to be environmentally costly. Consequently, researchers have turned their attention towards biological synthesis methods, also known as green synthesis, for producing nanoparticles [10]. These methods are being explored primarily due to their potential environmental benefits along with other compelling reasons. The emerging methods, known as green synthesis, involve harnessing the potential of plants, microorganisms, or fungi as a foundation for nanoparticle production. These approaches have been recognized as highly effective in utilizing the inherent biological components present in nature [11-13]. Plants, in particular, offer significant advantages for widespread adoption, as they are abundant, easily accessible. In the past few years, there have been notable achievements in utilizing various plant species to quickly and effectively produce gold, silver, copper, and other types of nanoparticles outside of living cells [14]. The extracts derived from aloe vera [15], Glycosmis pentaphylla leaf [16], and Limonia acidissima [17] have demonstrated successful outcomes in synthesizing ZnO NPs. The techniques employed for synthesizing nanoparticles from various plant components are comparatively simpler from a technical standpoint than chemical methods. As a result, biological materials assume a crucial role in nanoparticle synthesis, representing innovative alternatives to traditional chemical approaches. While the importance of utilizing plants for nanoparticle synthesis has been emphasized, regrettably, only a restricted number of studies have focused on this subject in Iraq [18,19]. Due to the significant variety of plant species found in Iraq, further research is necessary to explore this aspect.
Mohammadi et al. [20] used the aqueous extract of Euphorbia petiolata to synthesize ZnO NPs with a particle size range between 30-40 nm using the green synthesis method. Yassin et al. [21] also reported the preparation of ZnO NPs by using extracts of Origanum majorana. Another study was conducted where they utilized the Achillea wilhelmsii flower to extract cadmium oxide nanoparticles. The researchers found that certain compounds present in the extract, including tannins, flavonoids, alkaloids, and carotenoids, played a crucial role in reducing cadmium oxide ions and ensuring the stability of the resulting nanoparticles [22]. Furthermore, the blossoms of this particular species have been harnessed effectively in generating gold nanoparticles [23].
Achillea, a member of the Asteraceae plant family, possesses numerous medicinal and therapeutic characteristics. It is rich in polyphenolic compounds, phenolic compounds, sesquiterpene lactones, alkaloids, and flavonoids. Achillea is employed for various health purposes, including managing hypoglycemia, acting as a nerve tonic, alleviating hemorrhoids, treating diarrhea, providing antacid effects, acting as a carminative and appetizer, possessing anthelmintic properties, and serving as an antibacterial remedy [24-26]. Achillea Wilhelmsii is extensively utilized in various food items within Iraq [Fig. 1].
It has a rich history in traditional medicine, known for its diverse medicinal properties that include antioxidant, antifungal, antibacterial effects, and more [27,28]. Additionally, Achillea Wilhelmsii has been found to possess LDL-cholesterol-lowering properties and is abundant in oily and proteinaceous substances [29]. Given that the extract from this particular genus contains a high concentration of substances that possess antioxidant and reducing agents, it can be deemed significant and noteworthy in terms of its potential as a secure biological source for reducing zinc ions into nanoparticles. Therefore, this study was conducted with the aim of synthesizing green nanoparticles of ZnO using Achillea plants.
MATERIAL AND METHODS
In January 2023, Achillea Wilhelmsii flower shoots were collected from the Baghdad Forest & Agricultural Research Center and identified at the College of Agriculture, Baghdad University. The flower branches were dried in the shade before being washed with deionized water. To prepare the solution, 25 grams of dried flowers were placed in an Erlenmeyer flask and brought up to a volume of 100 milliliters. The mixture was boiled for 10 minutes and allowed to cool. The extract was then filtered using clean paper and 0.45 µm filters. Under reflux conditions at a temperature of 75°C, a volume of 40 mL of Achillea Wilhelmsii extract was slowly introduced to 60 mL of 1 M zinc nitrate solution. This addition was done drop by drop. The process lasted for 90 minutes and aimed to observe an alteration in hue caused by the phenomenon of the surface plasmon resonance effect. The changes were monitored using the ultraviolet-visible spectroscopy (UV-vis) technique. Simultaneously, white precipitates started forming. To separate the precipitation completely, centrifugation was performed at 8000 rpm. The resulting powder was then washed with methanol and distilled water to eliminate any potential contaminants. Subsequently, the powder underwent annealing in a muffle furnace at 450°C for a duration of 90 minutes [Fig. 2].
The nanoparticles obtained from this process were comprehensively studied via various analytical techniques such as UV-vis spectroscopy, X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), scanning electron microscopy (SEM), and Fourier-transform infrared spectroscopy (FTIR).
RESULTS AND DISCUSSION
UV-vis Spectrometry
The UV-vis of the sample revealed a distinct peak in light absorption at 370 nm (T80 series of UV-Visible Spectrophotometers, England) [Fig. 3]. This matches earlier findings that ZnO NPs absorb light maximally between 360-380 nm [30-32].
XRD analysis
XRD provides a distinct diffraction pattern for each unique crystalline solid, akin to a “fingerprint” for identifying materials. The X-ray diffraction pattern of the green synthesized ZnO NPs showed several distinct peaks between 0 and 90o (2θ), indicating the crystalline structure of the nanostructures. The detected signals at specific 2θ values of 31.8o, 34.5o, 36.3o, 47.6o, 56.6o, 62.9o, 66.4o, 68.0o, 69.1o, and 77.0o correspond to different crystallographic planes of ZnO (STOE Company, Germany) [Fig. 4]. The peak positions match well with standard diffraction data for crystalline monoclinic ZnO. The lack of extra peaks suggests high phase purity of the green synthesized ZnO NPs. The XRD results confirm the successful production of crystalline ZnO NPs using the green synthesis method, consistent with previous reports [19, 20, 31].
The average crystallite size of the synthesized ZnO NPs, as estimated from X-ray diffraction data, was determined to be 16 nm. This size aligns with the nanoparticle dimensions reported in prior studies [6].
Energy-Dispersive X-ray Analysis (EDX)
EDX analysis was used to semi-quantitatively determine the elemental composition of ZnO NPs produced from Achillea Wilhelmsii. The EDX results confirmed the presence of zinc and oxygen as the primary elements, with approximately 51.3% oxygen and 36.8% zinc by weight. Carbon was also detected at 13.2% by weight. The EDX spectrum showed dominant zinc peaks around 1 keV, consistent with ZnO NPs as the primary component. Additional smaller peaks at higher energies around 3 keV and 8.5 keV corresponded to the minor presence of other elements [Fig. 5].
Carbon presence in the spectrum signifies plant phytochemical group activity in limiting and reducing ZnO NPs synthesis [33]. At an energy of 1 keV in the ultra-peak spectrum, ZnO NPs are detected, aligning with other studies [19].
SEM analysis
The synthesized ZnO NPs were analyzed using SEM (JSM-6360) to determine their morphology and size. SEM images revealed spherical-shaped ZnO NPs with diameters ranging from 38-60 nm [Fig. 4]. The particles appeared clustered together with rough surfaces. These results closely matched findings by Jose et al. [15], who synthesized similar ZnO NPs using a Aloe Vera plant extract and observed spherical ZnO NPs of 38-60 nm diameter. Spherical ZnO NPs of 35-60 nm diameter were also reported using orange fruit peel extracts [34]. Overall, the spherical morphology and 38-60 nm diameter of the ZnO NPs synthesized here using Achillea Wilhelmsii align with previous reports that employed plant extracts like Aloe vera, Azadirachta indica, Abutilon indicum, and Clerodendrum inerme [35]. The SEM analysis confirms the synthesis of spherical-shaped ZnO NPs with diameters within the typical range of 38-60 nm using the Achillea Wilhelmsii plant extract.
FTIR analysis
The measurements of FTIR spectra analysis were performed at room temperature using the KBr pellet technique. Fig. 7(a) displays the FTIR spectrum for ZnO NPs synthesized via the bio-synthesis approach, while Fig. 7(b) represents the spectrum obtained from Achillea Wilhelmsii extract. In the Achillea Wilhelmsii extract spectrum, several absorption bands were observed at specific wavenumbers: 3747, 3340, 2927, 2362, 1645, 1431, 1066, and 522 cm-1. After synthesizing the ZnO NPs, these bands underwent a shift and appeared at slightly different wavenumbers: 3751, 3435, 2924, 2362, 1635, 1473, 1022, and 447 cm-1, respectively. The peak noted at 447 cm-1 in the lower energy zone is of particular note, as it indicates the bending vibrational mode of the ZnO bond in the produced nanoparticles.
The metal-oxygen region is between 400 and 600 cm-1. In the FTIR spectra, there is a broad peak in the higher energy region which can be attributed to the stretching of O-H bonds and the presence of alcohols and phenols that are hydrogen-bonded (at approximately 3340 and 3435 cm-1). The vibration band occurring around 2927 and 2924 cm-1 signifies the stretching of C-H bonds, implying the existence of an alkane group [36]. The enol form of 1,3-diketones and hydroxy aryl ketones is evidenced by medium and sharp peaks observed at around 2362 cm-1. Mononuclear aromatics, cis-tri substituted, and vinyl exhibit absorption peaks at about 1645 and 1635 cm-1 [37]. Vibrations corresponding to O-H bond stretching in the polyols group are observed at wavenumbers of (1431, 1473) cm-1. Lastly, Vibrations corresponding to stretching modes occur at around 1066 and 1022 cm-1, representing the stretching of C-N bonds in aliphatic amines.
Particle Size Analyzer
The dynamic light scattering analyzer is commonly used to examine and study particles, emulsions, or molecules that have been dispersed or dissolved in a liquid. It finds application in determining the sizes of metallic nanoparticles or quantum dots, as well as analyzing the estimated population of both large and small aggregates for small molecules. After obtaining a solution through interaction with distilled water, a volume of 1 mL was diluted to 10 mL and subjected to analysis using the PSA analyzer Model: 90Plus/BI-MAS. The findings revealed that the nanoparticles generated have a size range of approximately 35-218 nanometers, with the majority of particles measuring around 117 nm [Fig. 8].
CONCLUSION
This investigation synthesized ZnO NPs with Achillea Wilhelmsii extract, which possesses antioxidant and regenerative chemical entities. Nanoparticle specifications were determined via existing instrumentation. In conclusion, an effective, green, biological, inexpensive and sustainable protocol for synthesizing ZnO NPs has been established, utilizing Achillea Wilhelmsii extract as a reducing agent. Uv-vis, FTIR, XRD, SEM and EDX analysis definitively confirmed nanoparticle biosynthesis and characteristics. Benefits afforded by this method consist of rapid reaction times, simple one-pot preparation, direct and sustainable nanoparticle synthesis, avoidance of toxic chemicals, extra surfactants/reductants, organic solvents, and a simple work-up procedure.
ACKNOWLEDGEMENT
Our team wishes to sincerely thank all of the people who assisted with and supported the work required to successfully finish this project.
CONFLICT OF INTEREST
The authors declare that there is no conflict of interests regarding the publication of this manuscript.