A green approach to the facile synthesis of colloidal platinum nanoparticles by Preyssler polyoxometalate

Document Type: Research Paper

Authors

1 Department of Chemical Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran

2 Department of Chemical Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran.

3 Department of Chemical Engineering, Quchan University of Technology, Quchan, Iran

4 Department of Chemistry, Mashhad Branch, Islamic Azad University, Mashhad, Iran

10.22052/JNS.2019.02.007

Abstract

In the present study, platinum nanoparticles were synthesized through an effective, facile and green method using H14[NaP5W30O110], a Preyssler-structured polyoxometalate, under UV light irradiation. Preyssler plays the roles of photocatalyst, reducing agent and stabilizer in the synthesis of Pt nanoparticles. The effect of different parameters, i.e. time, propan-2-ol volume, pH, molar ratio of Preyssler to Pt ions ([Preyssler]/[Pt4+]) and temperature on the size of prepared nanoparticles were investigated. Under different conditions, platinum nanoparticles with minimum size of 13 nm were ultimately obtained. The nanoparticles were characterized by UV/Vis spectroscopy, particle size distribution, transmission electron microscopy and electron diffraction techniques. The results showed that the photocatalytic behavior of Preyssler was a propulsion factor in reducing the Pt4+ ions. The resultant NPs are covered with a Preyssler layer which contributes to the stabilization of NPs. It was shown that the subsequent increasing of NP size can be on account of partly increasing rate of NP growth compared to nucleation. Moreover, the stability of obtained nanoparticles was inspected.

Keywords


INTRODUCTION

Metal nanoparticles are clusters of corresponding metal atoms with distinctive characteristic features. Amongst them, platinum nanoparticles (Pt NPs) have attracted great attention in the fields of energy production [1-3], environmental protection [4-6] and medicine [7-9], due to their exceptional catalytic and optical properties. These nanoparticles have been applied in fuel cells [3], petroleum industries [5], catalytic converters [6], biosensors [8] and drug delivery [9].

So far, various chemical approaches have been exploited for the synthesis of colloidal Pt NPs, such as photochemical [10, 11], sonochemical [12], polyol [13, 14] and reverse microemulsion [15] methods. Most of these methods suffered from some drawbacks, including high cost, high temperature, tedious work-up procedure, long reaction times and environmental problems [13, 14]. For example, the reaction mixture generally contained three reagents, platinum precursor, reductant and stabilizer. The most common reductants were alcohols, citrate, hydrazine and formaldehyde [7, 11, 13, 14, 16], that could not be restored and inevitably entered into the environment. Besides, the polymeric reagents were used as stabilizer [10, 11, 14, 16], which can decrease the catalytic activity of prepared Pt NPs. Accordingly, they rarely follow the green chemistry criteria that encouraged scientists to investigate different alternative for nanoparticles synthesis.

Polyoxometalates (POMs) are transient metal-oxygen clusters with various structures and exhibit considerable redox and photocatalytic properties [17-25]. POMs are large molecules with high anionic charge, which can tolerate several-electron exchanges without any alteration in their structures [17, 20, 21, 26, 27]. They are a green kind material that are harmless to the environment with respect to safety, corrosiveness, low waste and specially, separability. Under photo irradiation, these compounds can act as both an oxidizer for organic materials (S) and a reducer of metal ions (M+) through Eqns. (1) and (2) respectively [20].

 (1)

 (2)

Consequently, many researchers have applied POMs for facile and green synthesis of highly surface-charged metal NPs, in which the POMs performed the multifunctional duties of photocatalyst, reducing and stabilizing agents [20, 22, 23, 25, 28-31]. POMs have different types, such as Keggin, Dawson, mixed valance, Preyssler, etc. with different chemical properties. Along with the various studies on the role of POMs in the synthesis of metal nanoparticles, Keggin and mixed-valance types of POMs have been exploited for the synthesis of Pt NPs. For instance, Troupis et al. have reported synthesis of Pt NPs at room temperature using H3[SiW12O40], a Keggin type of POMs [20]. In this regard, the role of Preyssler acid has been largely overlooked. This type of POM have remarkable properties, including strong Brönsted acidity with 14 acidic protons, high oxidation potential, high hydrolytic and thermal stability, non-corrosiveness, safety and substantial recyclability [25, 32]. In this assessment, we present our efforts for synthesizing Pt NPs with the assistance of Preyssler acid, H14[NaP5W30O110], using an one-pot reaction system in which Preyssler acts as photocatalyst, reductant and stabilizer with no need of surfactant.

MATERIALS AND METHODS

Synthesis of NPs

H2PtCl6 and propan-2-ol were obtained from Merck Company and used as received. Preyssler acid was synthesized according to the method described in previous work [33]. In a typical experiment, 50 mL of H2PtClsolution (2×10-4 M), Preyssler and propan-2-ol were placed into a spectrophotometer cell and deaerated with N2 gas. Then, the mixture was irradiated by UV light (125 W high pressure mercury vapor lamp) under continuous stirring. Temperature was regulated using water circulation around the cell. Ultimately, a colloid with a slight yellow color was appeared, indicating the formation of Pt NPs [34]. Similarly, several reactions were performed under different conditions to investigate the effect of different parameters, i.e. time, propan-2-ol volume, pH, molar ratio of Preyssler to Pt ions ([Preyssler]/[Pt4+]) and temperature.

Characterization

UV/Vis spectra of NPs were obtained using Avantes Avaspec-3648 single beam instrument. The size of NPs was determined by a particle size analyzer VASCO instrument (Cordouan technology). Nanoparticles were inspected using Transmission Electron Microscopy (TEM) via Philips CM-120 apparatus.

RESULTS AND DISCUSSION

Under UV irradiation, Preyssler acid was activated and simultaneously undertook the reduction of Pt ions and formation of stable NPs. In this process a charge transfer from propan-2-ol to Pt4+ ions occurs via Preyssler acid that features a considerable photocatalytic activity. Herein, propan-2-ol plays acts as a sacrificial agent. For concise investigations, the UV/Vis absorption spectrum of the reactants mixture is measured before starting of the reaction and representatively shown in Fig. 1. In this figure, there is only one peak near 260 nm wavelength ascribed to the characteristic absorption band of PtCl62- [35-37].

Depicted in Fig. 2, the spectra of the reaction mixture at different stages of irradiation consist of two peaks in the range of 211-217 nm and 260-278 nm. Appearance of the former is due to the surface plasmon resonance of Pt NPs [13, 34, 38]. The latter can be caused by acetone produced from alcohol oxidation and also by the residue of PtCl62- [13]. Up to 2 h of irradiation, the resonance intensity increased and then depleted. It can be due to the highest number of NPs which was achieved after 2 h [39]. More irradiation time led to aggregation of NPs, evidenced by a red shift and broadening particle size analyzing of the absorption peak of NPs after 5 h [13, 34]. This results were confirmed by particle size analyzing. After 2 and 5 h, the NPs with size of 20 and 93 nm were obtained respectively. In order to clarify the importance of the presence of Preyssler, a control experiment was performed between 2 mL propan-2-ol and H2PtCl6 (2×10-4 M) in the absence of Preyssler acid. After 2 h irradiation, no change were observed in the absorption peak of the reactants.

The UV-vis spectra of synthesized Pt NPs using different amounts of propan-2-ol are shown in Fig. 3. In these experiments, four different volumes of propan-2-ol were examined, while the other parameters were kept constant. The maximal resonance intensity was obtained by using 2 mL propan-2-ol, implying that the most populated colloid of NPs was formed. Indeed, altering the amount of propan-2-ol affects the nucleation rate [30]. Thus, the fraction of Pt atoms participates in nucleation, number of nuclei and consequently number of NPs in colloid changes. By employing 2 and 4 mL of propan-2-ol, nanoparticles with a size of 20 and 25 nm was formed respectively.

By the same experiments, the effect of pH was also investigated (Fig. 4). It was found that increasing pH caused to reduction of resonance intensity. Moreover, full-width at half-maximum (FWHM) of spectra at pH=7 was larger, as compared with lower amounts of pH. It was agree with the result of particle size analysis. At pH=2, a large number of NPs with average size of 20 nm were obtained, while at pH=7 a few NPs with size of 51 nm were produced. It is worth to note that lower pH values were found to be more effective in the synthesis of NPs. At low pH, the reduction of POMs can be catalytically enhanced by protons [40], followed by faster reduction of Pt ions. So, a large number of NPs with small size were produced.

The dependency of NP size to [Preyssler]/[Pt4+] and temperature was also examined. As displayed in Fig. 5, when [Preyssler]/[Pt4+] increased, the size of obtained NPs firstly decreased to 16 nm (at [Preyssler]/[Pt4+] = 0.001) and then, slightly increased. Indeed, increasing the [Preyssler]/[Pt4+] ratio introduces more POMs to the reaction media which can increase the rate of reaction in Eqn. (2). The faster reaction would resulted to the smaller NPs [30]. In addition, POMs can prevent growth of NPs, as stabilizer. Much more increasing of [Preyssler]/[Pt4+] (>0.001) led to higher coverage of POMs on the exterior surface of NPs and resulted to decreasing the rate of equation (2) [30].

Therefore, rising of [Preyssler]/[Pt4+] ratio up to 1 resulted in the formation of very fine NPs trapped in a matrix of Preyssler (as shown in Fig. 6). The nanoparticles in this situation did not have any fortune of growth.

Fig. 7 displays the variation of the size of obtained nanoparticles with temperature. As can be see, with temperature increasing, the size of nanoparticles followed the same trend as shown in Fig. 5. Reduction of nanoparticles size is due to the growing kinetic energy of POMs and Pt ions with temperature which improved the rate of equation (2) [39]. Subsequent increasing of NP size might be attributed to the partly increasing rate of nanoparticles growth compared to nucleation. Fig. 7 indicates that the minimum size of NPs is 13 nm, which was acquired at 42.5 °C. Particle size distribution of these nanoparticles is illustrated in Fig. 8. The inset in Fig. 8 shows the colloidal nanoparticles with a slight yellow color. Furthermore, TEM image of these NPs is shown in Fig. 9. It confirmed that the nanoparticles were formed with a uniform size. Also, the crystalline structure of Pt NPs was evidenced by ED pattern (the inset of Fig. 9).

In order to inspecting the stability of NPs, a control experiment was performed at a specific condition. Then absorption spectra of the prepared NPs was measured just at the end of the reaction (without aging) and also after 24 h aging. The results (see Fig. 10) indicated that no aggregation was discerned in the colloid. Furthermore, the TEM image of obtained Pt NPs (show in Fig. 11) clearly indicated that the nanoparticles were covered with a POM layer, which can stabilize the nanoparticles with their high negative charges.

CONCLUSIONS

Applying Preyssler acid as a green agent in the synthesis of Pt NPs, results in formation of highly stable NPs with uniform size. Preyssler acts as photocatalyst, reductant and stabilizer by oneself with no need to another contributing agent. The photocatalytic behavior of Preyssler was a propulsion factor in reducing the Pt4+ ions. The resultant NPs are covered with a Preyssler layer which contributes to the stabilization of NPs.

ACKNOWLEDGEMENTS

The authors gratefully acknowledge the personnel of Chemical Engineering Research Lab of Ferdowsi University of Mashhad and also the financial support of Iran Nanotechnology Initiative Council.

CONFLICTS OF INTEREST

The Authors declares that there is no conflict of interest.

 

 

1. Solla-Gullón J, Vidal-Iglesias FJ, Feliu JM. Shape dependent electrocatalysis. Annual Reports Section “C” (Physical Chemistry). 2011;107:263.

2. Christensen ST, Elam JW, Rabuffetti FA, Ma Q, Weigand SJ, Lee B, et al. Controlled Growth of Platinum Nanoparticles on Strontium Titanate Nanocubes by Atomic Layer Deposition. Small. 2009;5(6):750-7.

3. Sun C-L, Tang J-S, Brazeau N, Wu J-J, Ntais S, Yin C-W, et al. Particle size effects of sulfonated graphene supported Pt nanoparticles on ethanol electrooxidation. Electrochimica Acta. 2015;162:282-9.

4. Mayrhofer KJJ, Arenz M, Blizanac BB, Stamenkovic V, Ross PN, Markovic NM. CO surface electrochemistry on Pt-nanoparticles: A selective review. Electrochimica Acta. 2005;50(25-26):5144-54.

5. Campelo JM, Lee AF, Luque R, Luna D, Marinas JM, Romero AA. Preparation of Highly Active and Dispersed Platinum Nanoparticles on Mesoporous Al‐MCM‐48 and Their Activity in the Hydroisomerisation ofn‐Octane. Chemistry - A European Journal. 2008;14(19):5988-95.

6. Artelt S, Creutzenberg O, Kock H, Levsen K, Nachtigall D, Heinrich U, et al. Bioavailability of fine dispersed platinum as emitted from automotive catalytic converters: a model study. Science of The Total Environment. 1999;228(2-3):219-42.

7. Chen A, Holt-Hindle P. Platinum-Based Nanostructured Materials: Synthesis, Properties, and Applications. Chemical Reviews. 2010;110(6):3767-804.

8. Sun Y, He K, Zhang Z, Zhou A, Duan H. Real-time electrochemical detection of hydrogen peroxide secretion in live cells by Pt nanoparticles decorated graphene–carbon nanotube hybrid paper electrode. Biosensors and Bioelectronics. 2015;68:358-64.

9. Sawosz E, Chwalibog A, Szeliga J, Sawosz F, Grodzik M, Rupiewicz M, Niemiec T, Kacprzyk K. Visualization of Gold and Platinum Nanoparticles Interacting with Salmonella Enteritidis and Listeria Monocytogenes. Int. J. Nanomed., 2010; 5: 631-7.

10. Luo X, Imae T. Photochemical synthesis of crown-shaped platinum nanoparticles using aggregates of G4-NH2PAMAM dendrimer as templates. J Mater Chem. 2007;17(6):567-71.

11. Chen C-W, Akashi M. Synthesis, Characterization, and Catalytic Properties of Colloidal Platinum Nanoparticles Protected by Poly(N-isopropylacrylamide). Langmuir. 1997;13(24):6465-72.

12. Mizukoshi Y, Oshima R, Maeda Y, Nagata Y. Preparation of Platinum Nanoparticles by Sonochemical Reduction of the Pt(II) Ion. Langmuir. 1999;15(8):2733-7.

13. Herricks T, Chen J, Xia Y. Polyol Synthesis of Platinum Nanoparticles:  Control of Morphology with Sodium Nitrate. Nano Letters. 2004;4(12):2367-71.

14. Henglein A, Ershov BG, Malow M. Absorption Spectrum and Some Chemical Reactions of Colloidal Platinum in Aqueous Solution. The Journal of Physical Chemistry. 1995;99(38):14129-36.

15. Noh J-H, Meijboom R. Synthesis and catalytic evaluation of dendrimer-templated and reverse microemulsion Pd and Pt nanoparticles in the reduction of 4-nitrophenol: The effect of size and synthetic methodologies. Applied Catalysis A: General. 2015;497:107-20.

16. Bonet F, Delmas V, Grugeon S, Herrera Urbina R, Silvert PY, Tekaia-Elhsissen K. Synthesis of monodisperse Au, Pt, Pd, Ru and Ir nanoparticles in ethylene glycol. Nanostructured Materials. 1999;11(8):1277-84.

17. Yang W, Gao L-H, Wang K-Z. Photoelectric properties of polyoxometalate-based thin films – Recent advances and future perspective. Polyhedron. 2014;82:80-7.

18. Zhao J, Ding Y, Wei J, Du X, Yu Y, Han R. A molecular Keggin polyoxometalate catalyst with high efficiency for visible-light driven hydrogen evolution. International Journal of Hydrogen Energy. 2014;39(33):18908-18.

19. Keita B, Zhang G, Dolbecq A, Mialane P, Sécheresse F, Miserque F, et al. MoV−MoVIMixed Valence Polyoxometalates for Facile Synthesis of Stabilized Metal Nanoparticles: Electrocatalytic Oxidation of Alcohols. The Journal of Physical Chemistry C. 2007;111(23):8145-8.

20. Troupis A, Hiskia A, Papaconstantinou E. ChemInform Abstract: Synthesis of Metal Nanoparticles by Using Polyoxometalates as Photocatalysts and Stabilizers. ChemInform. 2010;33(31):no-no.

21. Mueller A, Peters F, Pope MT, Gatteschi D. ChemInform Abstract: Polyoxometalates: Very Large Clusters-Nanoscale Magnets. ChemInform. 2010;29(16):no-no.

22. Ayati A, Ahmadpour A, Bamoharram FF, Heravi MM. A Green and Simple Route for the Controlled-Size Synthesis of Gold Nanoparticles Using Preyssler Heteropolyacid. Synthesis and Reactivity in Inorganic, Metal-Organic, and Nano-Metal Chemistry. 2012;42(9):1309-14.

23. Ayati A, Ahmadpour A, Bamoharram FF, Heravi MM, Sillanpää M. Rate redox-controlled green photosynthesis of gold nanoparticles using H3 + x PMo12 − x V x O40. Gold Bulletin. 2012;45(3):145-51.

24. Ayati A, Ahmadpour A, Bamoharram F, Heravi M, Rashidi H, Tanhaei B. Application of a New Photocatalyst in the Preparation of Silver Nanoparticles and Investigating Their Photocatalytic Activity. J. Nanostruct. Chem., 2011; 2(1): 15-22.

25. Ayati A, Ahmadpour A, Bamoharram FF, Heravi MM, Rashidi H. Photocatalytic Synthesis of Gold Nanoparticles Using Preyssler Acid and Their Photocatalytic Activity. Chinese Journal of Catalysis. 2011;32(6-8):978-82.

26. Zhang J, Ting BP, Koh YT, Ying JY. Synthesis of Metallic Nanoparticles Using Electrogenerated Reduced Forms of [α-SiW12O40]4–as Both Reductants and Stabilizing Agents. Chemistry of Materials. 2011;23(21):4688-93.

27. Casañ-Pastor N. Polyoxometalates: from inorganic chemistry to materials science. Frontiers in Bioscience. 2004;9(1-3):1759.

28. Niu C, Wu Y, Wang Z, Li Z, Li R. Synthesis and shapes of gold nanoparticles by using transition metal monosubstituted heteropolyanions as photocatalysts and stabilizers. Frontiers of Chemistry in China. 2009;4(1):44-7.

29. Mandal S, Das A, Srivastava R, Sastry M. Keggin Ion Mediated Synthesis of Hydrophobized Pd Nanoparticles for Multifunctional Catalysis. Langmuir. 2005;21(6):2408-13.

30. Ayati A, Ahmadpour A, Bamoharram FF, Heravi MM, Rashidi H, Tanhaei B. Application of Molybdophosphoric Acid as Reducing Agent/Stabilizer in the Synthesis of Gold Nanoparticles under UV Irradiation. Int. J. NanoSci. Nanotechnol., 2011; 7(2): 87-93.

31. Khadempir S, Ahmadpour A, Hamed Mosavian MT, Ashraf N, Bamoharram FF, Mitchell SG, et al. A polyoxometalate-assisted approach for synthesis of Pd nanoparticles on graphene nanosheets: synergistic behaviour for enhanced electrocatalytic activity. RSC Advances. 2015;5(31):24319-26.

32. Ayati A, Tanhaei B, Bamoharram FF, Ahmadpour A, Maydannik P, Sillanpää M. Photocatalytic degradation of nitrobenzene by gold nanoparticles decorated polyoxometalate immobilized TiO 2 nanotubes. Separation and Purification Technology. 2016;171:62-8.

33. Bamoharram FF, Heravi MM, Roshani M, Jahangir M, Gharib A. Preyssler catalyst, [NaP5W30O110]14−: A green, efficient and reusable catalyst for esterification of salicylic acid with aliphatic and benzylic alcohols. Applied Catalysis A: General. 2006;302(1):42-7.

34. Chen S, Kimura K. Synthesis of Thiolate-Stabilized Platinum Nanoparticles in Protolytic Solvents as Isolable Colloids. The Journal of Physical Chemistry B. 2001;105(23):5397-403.

35. Hikosaka K, Kim J, Kajita M, Kanayama A, Miyamoto Y. Platinum nanoparticles have an activity similar to mitochondrial NADH:ubiquinone oxidoreductase. Colloids and Surfaces B: Biointerfaces. 2008;66(2):195-200.

36. Zhou M, Chen S, Ren H, Wu L, Zhao S. RETRACTED: Electrochemical formation of platinum nanoparticles by a novel rotating cathode method. Physica E: Low-dimensional Systems and Nanostructures. 2005;27(3):341-50.

37. Li F, Chai J, Yang H, Han D, Niu L. Synthesis of Pt/ionic liquid/graphene nanocomposite and its simultaneous determination of ascorbic acid and dopamine. Talanta. 2010;81(3):1063-8.

38. Flynn NT, Gewirth AA. Synthesis and characterization of molybdate-modified platinum nanoparticles. Physical Chemistry Chemical Physics. 2004;6(6):1310.

39. Henglein A. Preparation and Optical Aborption Spectra of AucorePtshelland PtcoreAushellColloidal Nanoparticles in Aqueous Solution. The Journal of Physical Chemistry B. 2000;104(10):2201-3.

40. Yang L, Shen Y, Xie A, Liang J, Li S, Zhang Q. Size- and Shape-Controlled Synthesis and Assembly of a Silver Nanocomplex in UV-Irradiated TSA Solution. European Journal of Inorganic Chemistry. 2006;2006(22):4658-64.

41. Shanmugam S, Viswanathan B, Varadarajan TK. A novel single step chemical route for noble metal nanoparticles embedded organic–inorganic composite films. Materials Chemistry and Physics. 2006;95(1):51-5.

42. Zhang J, Goh J-K, Tan W-T, Bond AM. Mechanistic Analysis of the Electrocatalytic Properties of Dissolved α and β Isomers of [SiW12O40]4-and Solid [Ru(bipy)3]2[α-SiW12O40] on the Reduction of Nitrite in Acidic Aqueous Media. Inorganic Chemistry. 2006;45(9):3732-40.