Recently alcohol fuel cells has been increased consideration because of their environmental friendliness, high energy conversion eﬃciency and low emissions [1,2]. Many effort have been made to improve the electro-oxidation performance of alcohols such as methanol, ethanol and propanol . Ethanol is known as an ideal material for fuel cells due to its high energy density, low toxicity, large production from renewable sources and transportation , but several main restrictions exist in the practical usage of ethanol in the field of fuel cells, such as low electro-oxidation activities, high cost of noble metal based catalysts, and so on [5,6]. Hence for reduce the cost of catalysts, Pt-free materials such as Pd have been studied [7,8].
As successor for valuable metals, non-noble metals, nickel and nickel compounds are noteworthy because of their low cost, electrochemical stability, resistance to poisoning, and high catalytic activity for electro-oxidation of ethanol. The catalysts for ethanol oxidation is more energetic in alkaline medium than acid medium [9–12]. In alkaline solutions nickel converted to Ni (OH) 2 and the Ni2+/Ni3+ redox show high catalytic activity for oxidation of some small organic compounds [13,14]. Nickel is an impressive and inexpensive catalyst for oxidation of small organic compounds including carbohydrates [15,16], methanol [17,18] and ethanol [19–24]. For example, nickel redox, Ni (OH) 2/NiOOH, formed on the nickel surface display high catalytic activity for oxidation of ethanol in alkaline media. Because of the low electrical conduction of these changed and accumulation of small Ni nanoparticles limited their electrocatalytic performance [25,26]. To solve the problems, Ni nanocrystals were dispersed and fixed on a solid support, usually using carbon materials as the matrix [27–29]. The electrocatalytic performance of the nanocomposites will be improved due to the highly conductive matrix, structural properties and fixation of Ni nanocrystals.
Graphite nanoﬁber (GNF) , carbon nanotubes (CNT) [31–34], carbon nanohorns  and carbon nanocoils  applied as carbon support for fuel cell usage. TiO2–carbon materials have been considered as catalyst support materials in fuel cell electrode .The nanostructured titania (TiO2) has usage in drug transfer, filters, solar cells, and biosensors because of its high specific surface area, chemical stability and biocompatibility [38–40]. Electrospinning is a simple technique, and used for many years to process polymer, metal oxides materials into one-dimensional (1D) structural ﬁbers such as TiO2 nanofiber .
TiO2 doping with transition metals ions such as V, Co, or Fe has been a popular method for modifing the photocatalytic performance of the catalyst [42–44]. However, some problems remain unresolved, for example, doped materials have thermal instability, an increase in the carrier-recombination probability, and photocorrosion . Non-metal (B, F, N, C etc.) doping has been proved to be more prosperous [27,46–49] particularly, in the manner of carbon doping, the C element is infiltrating to the lattice of TiO2 replacing a lattice O atom and form O–Ti–C species.
To the best of our knowledge, no study has been published so far reporting the electroanalytical applications of TiO2@C-Ni. We generate TiO2@C NFs mixing the electrospinning technique (for TiO2 NFs) and hydrothermal approach (for carbon layer). In this method glucose used as a carbon source and ﬁbrous TiO2@C core–shell nanocomposites as electro-catalyst supports for NiNPs. It’s a new catalyst that use in ethanol oxidation application based on these reasons. First, Ni nanoparticles, when well dispersed and with good particle size, show good catalytic activity for ethanol electro-oxidation due to ability of Ni to adsorb OH− ions to formation of Ni (OH)2. Second, the high electric conductivity of carbon boosts current collection. Third, a 1D TiO2 NFs provides accessibility for active species and catalysts and enhances the eﬀective mass transfer of reactants. Also, the use of Ni causes reduces in catalyst cost.
MATERIALS AND METHODS
The electrochemical measurements were done with a Zive lab potentiostat/galvanostat. A three-electrode system was used, where a glassy carbon (GC) electrode was used as the working electrode, a platinum wire as the counter electrode and saturated calomel electrode (SCE) as the reference electrode. An electrospinning device, FANAVARAN NANO-MEGHYAS Model: ES1000 with controllable feeding rate and DC voltage range of 5 kV to 30 kV was used to formation nanofiber.
TiO2@C nanofibers were synthesized in our laboratory which their synthesis explained here. Acetic acid, titanium tetraisopropoxide (TTIP), polyvinylpyrrolidone (PVP), ethanol, glucose, NaOH were analytical grade from Merck (Darmstadt, Germany).
Preparation of TiO2 NFs
Firstly, 0.38 g poly (vinyl pyrrolidone) powder (PVP, Mw = 1300000) was added to a mixture of 9 mL absolute ethanol and 2.4 mL acetic acid in a bottle. The solution was stirred for 2 h to provide a homogeneous solution. Then 360 µL Ti (OC4H9)4 was added to the solution, the mixture was stirred for 3 h to make precursor solution. The above solutions were drawn into a syringe that was connected to the 15 kV voltage and distance between the needle tip and collector was 15 cm. The as-collected nanoﬁbers were calcined and remained for 2 h at 550 ºC to form TiO2 NFs.
Preparation of TiO2@C NFs
TiO2@C NFs were prepared by hydrothermal method. It was explained as follows: glucose (0.6 g) and TiO2 NFs (15 mg) were put into a teﬂon-lined stainless steel autoclave of 25 mL capacity which including 20 mL deionized water to make glucose solution with the concentration of 30 g L -1. After powerful stirring for 10 min, the mixture was then stirred to form a milk like suspension, and hydrothermally treated at 180 ºC for 4 h. After reaction, the autoclave was cooled in air, and the suspensions were isolated by ﬁltration, washed with water several times and dried in oven at 80 ºC for 4 h.
Preparation of the electrode
In these work, Ni nanoparticles were synthesized by electrochemical method .To reach the best position in the preparation of TiO2@C- Ni /GC electrode, at first, the surface of GC electrode was polished on a polishing cloth with 0.05 mm alumina powder and then was washed with deionized water. GC electrode was created with Ni nanoparticle and TiO2 @C nanofiber in two steps:
First, about 2.0 mg of TiO2 @C nanofibers were dispersed in 0.45 mL ethanol, 0.45 mL water and 100 µL nafion an ultrasound bath for 30 min then a volume of 3.0 µL of the suspension was applied directly on a GC electrode surface and dried in air, then the potentiostatic deposition of nickel nanoparticle on the TiO2@C- Ni / GC electrode from an aqueous solution of 60 mM Ni+2 by controlled potential coulometry (CPC) applying a constant potential electrolysis at -0.6 V for 60 seconds was used, preparation of TiO2-Ni/GC electrode is same as the mentioned electrode.
RESULTS AND DISCUSSION
Characterization of TiO2@C- Ni
The morphologies of the TiO2 nanoﬁbers, TiO2@C nanofibers, TiO2 NFs-Ni and TiO2@C NFs-Ni have been investigated by scanning electron microscopy (SEM) (Fig. 1) and X-Ray diffraction (XRD) patterns (Fig. 2).
SEM image shows that the lengths of these nanoﬁbers were about several micrometers and the surface of TiO2 nanoﬁbers was clear Fig 1A. After done hydrothermal, the nanoﬁbrous morphology shown in Fig. 1B remained unchanged and the surface morphology of TiO2@C NFs catalysts was found to be uniform and porous surface, TiO2 nanocrystals encapsulated in carbon matrices. The TiO2 nanoﬁbers can be seen as an intermediate yield in the preparation of TiO2@carbon nanoﬁbers. Fig 1C shows SEM image of TiO2@C- Ni that decorated with carbon matrices and Ni nanoparticles, NiNPs existing on the surface of TiO2@C. Fig 1D shows SEM image of TiO2 (NF) that decorated with Ni nanoparticles, it can be seen NiNPs existing on the surface TiO2 nanofiber.
The X-ray diffraction (XRD) patterns of the TiO2 NFs,TiO2@C NFs, TiO2 NFs-Ni and TiO2@C NF-Ni are shown in Fig. 2. As observed in Fig. 2, TiO2 NFs show six reﬂection peaks appeared at 2Ө = 25.4 (101), 37.9 (004), 48.0 (200), 54.8 (105), 55.4 (211) and 63.8 (112), respectively, which were attributed to the anatase TiO2. The diffraction peaks of the TiO2 nanoﬁbers were sharp and intense, indicating the highly crystalline character of the nanoﬁbers. The curves of TiO2@carbon nanoﬁbers, TiO2 (NF)-Ni (NPs) and TiO2@carbon (NFs)-Ni also exhibited the diffraction peaks of anatase TiO2. And, the graphitic carbon peak at 2Ө = 25.6 for TiO2@carbon nanoﬁbers was too weak to see . To verify whether Ni (NPs) was deposited to TiO2 and TiO2@carbon NF during the electrochemical process, XRD patterns of the TiO2 (NF)-Ni (NPs) and TiO2@carbon (NFs)-Ni were recorded and compared. The diffraction peaks at 51.5° corresponded to the (2 0 0) facets of the Ni crystal, respectively .
Electrocatalytic effect of TiO2@C- Ni for oxidation of ethanol
The impression of scanning rates on the CV response of the TiO2@C- Ni/GC electrode was investigated in 0.1 M NaOH solution, and the results are shown in Fig. 3A. For TiO2@C- Ni/GC electrode redox with increased scanning rates peak current increased, inset Fig. 3A shows both anodic and cathodic peak currents have linear response to the scan rates ranging from 0.01 - 0.3 V s -1. This can be ascribed to the electrochemical activity of an immobilized redox on the surface with a surface-controlled process . The surface coverage г* can be estimated according this equation :
where г* is the surface coverage of redox sample, n is the number of transferred electrons (1 for Ni2+/Ni3+), ν is the scan rate, A is the surface area of the electrode, all other symbols have their conventional concept. The surface coverage of TiO2@C- Ni /GC electrode was estimated to be г*a = 6.22× 10-7 mol cm-2for anodic peak currents.
Fig. 4 shows the comparative CV responses from the electrochemical oxidation of 2 M ethanol at the TiO2@C- Ni /GC in 0.1 M NaOH (curve d), TiO2- Ni /GC in 0.1 M NaOH and 2 M ethanol curves (c), and (b) and (a) are the voltammograms of TiO2@C- Ni /GC and bare GCE, respectively, curve (b) in 0.1 M NaOH, curve (a) bare GCE in 0.1 M NaOH with 2 M ethanol. It clear that the current of catalyst in 2 M ethanol at scan rate of 100 mV s-1 is higher than other electrodes. Denoting that the TiO2@C- Ni /GC catalyst can oxidation ethanol, the enhanced electrocatalytic activity of TiO2@C- Ni /GC is due to the nanofibrous morphology increase the activity. To investigate the roles of C on TiO2 surface in the electrochemical oxidation of ethanol, the cyclic response of ethanol at the TiO2- Ni /GC (curve c) and TiO2@C- Ni /GC (curve d) electrodes were recorded. The results indicated that the presence of C on TiO2 surface exhibited 58.66%, improvement the peak current for ethanol. Although, the specific surface area of the nanoparticles is more than the nanofibers but the large axial ratio of the nanofibers increases the electrons transfer with the catalyst which results in modified the electrocatalytic process , and carbon materials as the matrix improve the conductivity.
The chronoamperometry method was utilized for comparison of the effect of different electrodes in ethanol oxidation. Fig. 5 shows the results of chronoamperometry measurements of TiO2@C- Ni /GC electrode in 0.1 M NaOH and 2 M ethanol (d), TiO2@C- Ni /GC electrode in 0.1 M NaOH (c), GC electrode in 0.1 M NaOH and 2 M ethanol (b), GC electrode in 0.1 M NaOH (a). The results showed that the TiO2@C- Ni /GC electrode in 0.1 M NaOH and 2 M ethanol electrode have high current in comparison with other electrodes. This because of the electrocatalytic properties of nanofibers in the TiO2@C- Ni /GC electrode for ethanol oxidation, and the improvement in the activity of TiO2@C- Ni /GC electro-catalyst for ethanol oxidation maybe related to the uniform dispensation of metal nanoparticles on the TiO2@C NFs support. It is said that the addition of Ni decreased the overpotential and NiOOH formed on the surface of the catalyst, increases the catalytic activity for ethanol oxidation which is in according to the results of cyclic voltammetry of ethanol oxidation.
Fig. 6 shows CV of different ethanol concentration in 0.1 M NaOH and scan rate 50 mVs-1. The results show the good electrocatalytic activity of nanofibers. Increasing the ethanol concentration in the alkaline solution increase the anodic current, with increasing ethanol concentration the peak potential shifted positively, showing kinetic limitation. Anodic peak in the reverse scan in the ethanol oxidation is because of the more oxidation of ethanol molecules due to regeneracy of the active (Ni+2/Ni+3) on the electrode surface which were coating by intermediates, ethanol molecules or reaction products in the forward scan. Therefore, the efficient utilization of high alcohol contents is an important performance parameter for corresponding catalysts. Inset (A) shows plots of the anodic peak currents (Ip) were linearly dependent on concentration of ethanol.
Fig. 7 shows the influence of the scan rate on the electrocatalytic activity of 2 M ethanol by TiO2@C-Ni/GC electrode and 0.1 M NaOH in the range of 0.1 to 0.9 V s-1. It can be seen, the anodic current increases with increasing the scan rate. As shown in (Inset A in Fig 6); plots of the anodic peak currents (Ip) were linearly dependent on ν1/2 in the range of 0.1 to 0.9 V s-1; this linear relationship display that the nature of the redox process was controlled by diffusion manner.
In this paper, we reported a victorious method to generate TiO2@C NFs, glucose used as a carbon source and present here ﬁbrous TiO2@C core–shell nanocomposites and new method for ethanol oxidation based on Ni nanoparticles (NiNPs) decorated TiO2@C (NFs) is presented. TiO2@C-Ni is new catalyst that exhibits performance in ethanol oxidation application based on these reasons. First, Ni nanoparticles, when well dispersed and with good particle size, show good catalytic activity for ethanol electro-oxidation due to ability of Ni to adsorb OH− ions in the form of Ni (OH)2. Second, the high electric conductivity of carbon boost current collection. Third, a 1D TiO2 NFs provides the maximum accessibility for active species and catalysts and enhances the eﬀective mass transfer of reactants due to the large axial ratio of the nanofibers. This work opens new avenue to synthesize more effective catalyst involve nanofiber to be applied in ethanol oxidation process.
CONFLICT OF INTEREST
The authors declare that there are no conflicts of interest regarding the publication of this manuscript.The authors wish to thank the Yazd University Research Council, IUT Research Council and Excellence in Sensors for financial support of this research.
1. Mohanraju K, Kousik G, Cindrella L. Surfactant free synthesis of high surface area Pt@PdM3 (M = Mn, Fe, Co, Ni, Cu) core/shell electrocatalysts with enhanced electrocatalytic activity and durability for PEM fuel cell applications. New Journal of Chemistry. 2016;40(10):8681-95.
10. Tripković AV, Popović KD, Grgur BN, Blizanac B, Ross PN, Marković NM. Methanol electrooxidation on supported Pt and PtRu catalysts in acid and alkaline solutions. Electrochimica Acta. 2002;47(22-23):3707-14.
11. Spendelow JS, Lu GQ, Kenis PJA, Wieckowski A. Electrooxidation of adsorbed CO on Pt(111) and Pt(111)/Ru in alkaline media and comparison with results from acidic media. Journal of Electroanalytical Chemistry. 2004;568:215-24.
12. Cohen JL, Volpe DJ, Abruña HD. Electrochemical determination of activation energies for methanol oxidation on polycrystalline platinum in acidic and alkaline electrolytes. Phys Chem Chem Phys. 2007;9(1):49-77.
15. Cataldi TRI, Desimoni E, Ricciardi G, Lelj F. Study of the nickel-based chemically modified electrode obtained by electrochemical deposition of an NiII-tetramethyl-dibenzo-tetraaza  annulene complex. Redox catalysis of carbohydrates in alkaline solutions. II. Electroanalysis. 1995;7(5):435-41.
16. Mazloum-Ardakani M, Amin-Sadrabadi E, Khoshroo A. Enhanced activity for non-enzymatic glucose oxidation on nickel nanostructure supported on PEDOT:PSS. Journal of Electroanalytical Chemistry. 2016;775:116-20.
17. Ciszewski A, Milczarek G. Glassy carbon electrode modified by conductive, polymeric nickel(II) porphyrin complex as a 3D homogeneous catalytic system for methanol oxidation in basic media. Journal of Electroanalytical Chemistry. 1997;426(1-2):125-30.
18. Zhang M, Yan Z, Sun Q, Xie J, Jing J. Synthetic core–shell Ni@Pd nanoparticles supported on graphene and used as an advanced nanoelectrocatalyst for methanol oxidation. New Journal of Chemistry. 2012;36(12):2533.
19. Fleischmann M, Korinek K, Pletcher D. The kinetics and mechanism of the oxidation of amines and alcohols at oxide-covered nickel, silver, copper, and cobalt electrodes. Journal of the Chemical Society, Perkin Transactions 2. 1972(10):1396.
22. Hayes ET, Bellingham BK, Mark HB, Galal A. An amperometric aqueous ethanol sensor based on the electrocatalytic oxidation at a cobalt-nickel oxide electrode. Electrochimica Acta. 1996;41(2):337-44.
26. Liu Z, Li Z, Wang F, Liu J, Ji J, Wang J, et al. Synthesis of multi-walled carbon nanotube supported nickel catalysts by hydrazine reduction and their electrocatalytic activity on ethanol electro-oxidation. Materials Letters. 2011;65(23-24):3396-8.
27. Wang H, Yang Y, Wei J, Le L, Liu Y, Pan C, et al. Effective photocatalytic properties of N doped Titanium dioxide nanotube arrays prepared by anodization. Reaction Kinetics, Mechanisms and Catalysis. 2012;106(2):341-53.
28. Danaee I, Jafarian M, Forouzandeh F, Gobal F, Mahjani M. Electrocatalytic oxidation of methanol on Ni and NiCu alloy modified glassy carbon electrode. International Journal of Hydrogen Energy. 2008;33(16):4367-76.
29. Cheon S-Y, Park S-Y, Rhym Y-M, Kim D-H, Koo Y-S, Lee J-H. Electroless Nickel Plating on Fibers for the Highly Porous Electrode. Journal of Electrochemical Science and Technology. 2010;1(2):117-20.
31. Li W, Liang C, Zhou W, Qiu J, Zhou, Sun G, et al. Preparation and Characterization of Multiwalled Carbon Nanotube-Supported Platinum for Cathode Catalysts of Direct Methanol Fuel Cells. The Journal of Physical Chemistry B. 2003;107(26):6292-9.
32. Maiyalagan T. Synthesis and electro-catalytic activity of methanol oxidation on nitrogen containing carbon nanotubes supported Pt electrodes. Applied Catalysis B: Environmental. 2008;80(3-4):286-95.
33. Raoof J-B, Hosseini SR, Rezaee S. Preparation of Pt/poly(2-Methoxyaniline)/multi-walled carbon nanotube nanocomposite and its application for electrocatalytic oxidation of methanol. Journal of Molecular Liquids. 2014;200:196-204.
34. Alcohol D, Cell F. MULTI-WALLED CARBON NANOTUBES SUPPORTED Pt-Fe CATHODIC CATALYST FOR DIRECT METHANOL FUEL CELL Wenzhen Li. 2004;82(2):235–240.
35. Yoshitake T, Shimakawa Y, Kuroshima S, Kimura H, Ichihashi T, Kubo Y, et al. Preparation of fine platinum catalyst supported on single-wall carbon nanohorns for fuel cell application. Physica B: Condensed Matter. 2002;323(1-4):124-6.
38. Mazloum-Ardakani M, Beitollahi H, Amini MK, Mirjalili B-F, Mirkhalaf F. Simultaneous determination of epinephrine and uric acid at a gold electrode modified by a 2-(2,3-dihydroxy phenyl)-1, 3-dithiane self-assembled monolayer. Journal of Electroanalytical Chemistry. 2011;651(2):243-9.
39. Mazloum-Ardakani M, Khoshroo A, Taghavinia N, Hosseinzadeh L. Surface passivation of titanium dioxide via an electropolymerization method to improve the performance of dye-sensitized solar cells. RSC Advances. 2016;6(15):12537-43.
40. Ehteram A, Hamadanian M, Jabbari V. Fabrication of Novel High Potential Chromium-Doped TiO2 Nanoparticulate Electrode-based Dye-Sensitized Solar Cell ( DSSC ). 2015;5:443–453.
41. Naderizadeh B, Moghimi A, Shahi M. Electrospun Nitrocellulose and Composite Nanofibers. 2012;2:287–293.
44. Nasralla N, Yeganeh M, Astuti Y, Piticharoenphun S, Shahtahmasebi N, Kompany A, et al. Structural and spectroscopic study of Fe-doped TiO2 nanoparticles prepared by sol-gel method. Sci Iran [Internet]. 2013;20(3):1018–1022. Available from: http://dx.doi.org/10.1016/j.scient.2013.05.017
45. Choi W, Termin A, Hoffmann MR. The Role of Metal Ion Dopants in Quantum-Sized TiO2: Correlation between Photoreactivity and Charge Carrier Recombination Dynamics. The Journal of Physical Chemistry. 1994;98(51):13669-79.
47. Salarian A-A, Hami Z, Mirzaei N, Mohseni SM, Asadi A, Bahrami H, et al. N-doped TiO2 nanosheets for photocatalytic degradation and mineralization of diazinon under simulated solar irradiation: Optimization and modeling using a response surface methodology. Journal of Molecular Liquids. 2016;220:183-91.
51. Yang L, Luo S, Liu S, Cai Q. Graphitized Carbon Nanotubes Formed in TiO2 Nanotube Arrays: A Novel Functional Material with Tube-in-Tube Nanostructure. The Journal of Physical Chemistry C. 2008;112(24):8939-43.
52. Ni Y, Jin L, Zhang L, Hong J. Honeycomb-like Ni@C composite nanostructures: synthesis, properties and applications in the detection of glucose and the removal of heavy-metal ions. Journal of Materials Chemistry. 2010;20(31):6430.
54. Bard AJ, Faulkner LR. Fundamentals and applications. Electrochem Methods, 2nd ed; Wiley New York. 2001;
55. Barakat NAM, El-Newehy MH, Yasin AS, Ghouri ZK, Al-Deyab SS. Ni&Mn nanoparticles-decorated carbon nanofibers as effective electrocatalyst for urea oxidation. Applied Catalysis A: General. 2016;510:180-8.